is produced from GPPS Polystrene, color, talc and flame retardant.
Firstly the machine is heated and it takes 3-4 hours.
When the machine is heated sufficiently, gas pumps are kept ready by starting the motors of the gas pumps. uses 3 different gases which are CO2, R152A and Dimethyl ether DME to get high quality foam structure.
Then the raw materials are going into one main silo according to percentage.
After that the materials start to extrude. Materials go through different processes after the extrusion process.
Which are;
• Longer side edge trimming and board cutting,
• Waffled surface of XPS boards,
• Inkjet printer for product labeling,
• Short side edge trimming
• Packaging

Also this unit allows us to produce 3 different widths which are 0,6m – 0,9m – 1,2m and with this unit we can set the thickness of XPS boards between16-120 mm.
When the process finished there is some material which can be recycled so the unit sends the materials to the recycled unit after that the materials are put into production again. So we can say is produced with 100% recyclable zero-waste technology.

Thickness (mm)203040506080100120
Number per pack20141087543
m² per pack 1250×6001510,57,565,253,7532,25
m² per pack 2500×6003021151210,57,564,5
ThicknessThermal Conductivity
coefficient λ (W/mK)
Heat transfer resistance
R (mK/W)
20mm0,029340,68
30mm0,030510,98
40mm0,028801,39
50mm0,031681,58
60mm0,028782,09
80mm0,031652,53
100mm0,032443,08
120mm0,035003,42
thermal features
PropertiesThickness
20-120mm
Standard
1VOLUME MASS [kg/m3]28-40BAS EN
1602:2014
2Compressive strength at 10% deformation [kPa]250-500BAS EN
826:2014
3Flexural strength [kPa]300-1000BAS EN
12089:2014
4Tensile strength [kPa]250-500BAS EN
1607:2014
5FlammabilityCLASS EBAS EN ISO
11925-2:2011
BAS EN ISO
11925-2/Corr1:2012
BAS EN 13501-1+A:2010*
test results
1. PHYSICAL AND MECHANICAL PROPERTIES TICKNESS (mm) Standard
20 30 40 50 60 80 100 120
1.1 Volume mass (kg/m3)
-average values-
39,97 30,41 34,77 30,89 37,54 32,51 35,22 29,98 BAS EN 1602:2014
1.2 Compressive strength at
10% deformation [kPa]
-average values-
143,6 242,7 173,1 374,3 161,0 372,9 356,7 260,1 BAS EN 826:2014
1.3 Flexural strength [kPa]
-average values-
1010,1 462,3 480,9 343,3 564,6 462,9 322,5 268,6 BAS EN 12089:2014
1.4 Tensile strength [kPa]
-average values-
337,0 351,8 279,5 238,6 248,9 545,2 292,0 445,4 BAS EN 1607:2014
GIT Tuzla Lab Institute – Test results

×
img

    Get In Touch

    Contact Info

    Phone number

    +387 31 717 210

    Email address

    info@temax-xps.com

    Address info

    Dusine Industrial Zone no. 17 Orašje 76270 Bosnia and Herzegovina